WL-172B Corrosion Resistance Water Soluble Epoxy Ester Resin For Metal Surfaces

Basic Information
Place of Origin: china
Brand Name: WeiLi Resin®
Certification: ISO9001
Model Number: WL-172B
Minimum Order Quantity: 5000KG
Price: Negotiable
Packaging Details: 200kg/drum
Delivery Time: 14 work days
Payment Terms: L/C, T/T
Supply Ability: 500t/month
Detail Information
Solid Content: 74±2.0 Type Of Polymer: Wsterborne Epoxy Ester Resin
Viscosity: ≤200 Apperance: Brown Viscous Liquid
Highlight:

Corrosion Resistance Water Based Epoxy Resin

,

anti Corrosion Water Based Epoxy Resin

,

Water Soluble Epoxy Ester Resin


Product Description

Waterborne Epoxy Ester Resin WL-172B

 

Key words: water soluble epoxy ester resin for industrial coatings(red iron oxide primer), low cost, one component, fast drying

A red iron oxide primer and topcoat made of the water soluble epoxy ester resin WL-172B have high-performance, single-component, quick-dry, rust preventive formulated for use on ferrous metal substrates. It provides corrosion resistance for both interior and exterior steel surfaces. It is formulated to provide lasting rust and corrosion resistance on a variety of interior and exterior metal surfaces and may be top coated with water-based or alkyd/oil-based finishes. This primer offers excellent coverage, spreads evenly, resists sagging, is abrasion resistant, and provides unsurpassed durability.

 

 

Product Properties:

Self-emulsifying process, no emulsifier, excellent water resistance and corrosion resistance;

This product can be oxidized and cross-linked to form film, which can replace the traditional solvent based alkyd and epoxy ester resin;

Paint making process is similar to that of traditional solvent based paint, the resin can be grinded;

Good mechanical stability and storage stability.

WL-172B Corrosion Resistance Water Soluble Epoxy Ester Resin For Metal Surfaces 0

 

Resin Composition:

Waterborne resin, cosolvent, neutralizer

 

Typical Data:

Item WL-172B Test Method
Appearance Brown viscous liquid Visual Observation
Non-Volatile Matter ( %) 74±2.0

GB/T1725-2007

( 30min@120℃)

Viscosity (25℃, mPa.s) ≤200

GB/T 21059-2007

NDJ-79 Rotational Viscometer

Dilute with PM by 1:1 ratio, then test

 

 

Recommending WL-172B high performance waterborne epoxy ester resin

WL-172B Iron Oxide Red Primer

Reference Formula:

1 WL-172B
2 N,N-DMEA
3 Deionized Water
4 Dispersing Agent
5 Defoamer
6 Attapulgite
7 Iron Oxide Red
8 Zinc Sulphate
9 Precipitated Barium Sulphate
10 Deionized Water
11 WL-172B
12 N,N-DMEA
13 Drier
14 Sodium Nitrite
15 Deionized Water
16 Substrate Wetting Agent
17 Thickener
 

 

 

WL-172B Corrosion Resistance Water Soluble Epoxy Ester Resin For Metal Surfaces 1

 

Performance Data:

No. Test Item Test Data Test Standard
1 Original Paint Appearance No lumps, stir evenly Visual Observation
2 Paint Film Color Iron red color Visual Observation
3 Original Paint Viscosity(25℃)Ku 80-90 GB/T9269-2009
4 pH 8-9 GB8325-1987
5 Fineness μm <35 GB/T6753.1-2007
6 Non-Volatile Matter Content % 48 GB/T1725-2007
7 Surface Drying Time ≤20min GB1728-79
8 Hard Drying Time ≤5hrs GB1728-79
9 Gloss 10 GB/T9754-2007
10 Hardness (Pencil Method) HB GB/T6739-1996
11 Flexibility 1mm GB/T6742-2007
12 Impact Resistance kg.cm 50 GB/T1732-1993
13 Double Pendulum Hardness 0.58 GB/T1730-2007
14 Adhesion (Cross-Cut Method) 1grade GB/T9286-1998
15 Storage Stability 50℃*4 weeks,no layering, no sedimentation ————

ron Oxide Red Primer Initial Water Resistance

Substrate:tinplate

Film thickness:23±3μm

 

Time Water Drenching Test Data
Air Drying 24hrs 48hrs no abnormalities
Air Drying 72hrs 96hrs no abnormalities
Air Drying 168hrs 168hrs no abnormalities
 

 

Iron Oxide Red Primer Anti- Corrosive Properties

Substrate:carbon steel plate

Film thickness:45±5μm

 

Item Test Data
Salt fog resistance 72hrs no abnormalities
Salt water resistance 120hrs no abnormalities
 

one component Waterborne Epoxy Ester Resin For Red Oxide Primer and Topcoat,Cost effective 0

one component Waterborne Epoxy Ester Resin For Red Oxide Primer and Topcoat,Cost effective 1

one component Waterborne Epoxy Ester Resin For Red Oxide Primer and Topcoat,Cost effective 2

one component Waterborne Epoxy Ester Resin For Red Oxide Primer and Topcoat,Cost effective 3

one component Waterborne Epoxy Ester Resin For Red Oxide Primer and Topcoat,Cost effective 4

 

WL-172B Iron Oxide Red Primer

Reference Formula:

 

1 WL-172B
2 N,N-DMEA
3 Deionized Water
4 Dispersing Agent
5 Defoamer
6 Attapulgite
7 Titanium Dioxide
8 Carbon Black
9 Precipitated Barium Sulphate
10 Deionized Water
11 WL-172B
12 N,N-DMEA
13 Drier
14 Deionized Water
15 Substrate Wetting Agent
16 Thickener
 

 

Performance Data:

 

No. Test Item Test Data Test Standard
1 Original Paint Appearance No lump, stir evenly Visual Observation
2 Paint Film Color Gray Visual Observation
3 Original Paint Viscosity(25℃)Ku 80-90 GB/T9269-2009
4 pH 8-9 GB8325-1987
5 Fineness μm <30 GB/T6753.1-2007
6 Non-Volatile Matter Content % 48 GB/T1725-2007
7 Surface Drying Time ≤3min GB1728-79
8 Hard Drying Time ≤16hrs GB1728-79
9 Gloss 90-92 GB/T9754-2007
10 Hardness(pencil method) HB GB/T6739-1996
11 Flexibility 1mm GB/T6742-2007
12 Impact Resistance kg.cm 50 GB/T1732-1993
13 Double Pendulum Hardness 0.4 GB/T1730-2007
14 Adhesion(Cross-Cut Method) 1grade GB/T9286-1998
 

High Gloss Gray Topcoat Hardness Increase

Substrate:glass pane

Film thickness:23±3μm

Ambient temperature:25±5℃

Ambient humidity:50±2%

 

Double Pendulum Hardness(glass pane)
Time Drier 0.52% Drier 0.85%
24hrs 0.19 0.22
48hrs 0.25 0.27
72hrs 0.28 0.32
120hrs 0.53 0.53
 

High Gloss Gray Topcoat Initial Water Resistance

Substrate:tinplate

Film thickness:23±3μm

 

Time Water drenching before adjustment Water drenching after adjustment
Air Drying 24hrs 24hrs no abnormalities 48hrs no abnormalities
Air Drying 72hrs 44hrs no abnormalities 56hrs no abnormalities
Air Drying 168hrs 96hrs no abnormalities 144hrs no abnormalities
 
 