Corrosion Resistance Water Based Epoxy Emulsion For Flooring Coat Anti-Rust Coat

Basic Information
Place of Origin: china
Brand Name: WeiLi Resin®
Certification: ISO9001
Model Number: WL-213
Minimum Order Quantity: 5000KG
Price: Negotiable
Packaging Details: 200kg/drum
Delivery Time: 14 work days
Payment Terms: L/C, T/T
Supply Ability: 500t/month
Detail Information
Non-volatile Value(%): 50±2 Viscosity(m Pa·s): ≤2000
PH Value: 4.0~8.0 Epoxy Value(for Solid): 0.18~0.22
Exterior: Ivory Uniform Fluid Film Thickness: 50-60um
High Light:

amine curing agents


epoxy resin hardener

Product Description

Water Based Epoxy Emulsion WL-213


WL-213 is a kind of two-component waterborne epoxy resin, cooperated with amine curing agent, it can provide excellent corrosion resistance, currently, the combination of WL-213 and curing agent WL-140 produced by our company has been adopted by Shitupaint.

This product has the following features:

  1. Apply to primer, middle coat and finish topcoat
  2. Innovative water-based system, inline with strict emission regulations
  3. Available for 2k zinc rich primer
  4. It can be used in container, ship and other industries



Product components:

Epoxy resin cosolvent water

item WL-213 Test method
exterior Ivory uniform fluid visual
Non-volatile value(%) 50±2 GB/T1725-2007
viscosity(m Pa·s) ≤2000 NDJ-79 rotary viscosimeter
pH value 4.0~8.0 GB 8325-1987
Epoxy value(for solid) 0.18~0.22 Hydrochloric acidacetone solution















The typical data of product:



Product characteristics:

  • Free of heavy metal
  • Excellent anti-rust, anti-corrosion performance;
  • Excellent properties of water resistance and salt fog resistance;
  • The superior application properties.



This product belongs to water borne epoxy latex which can prepare water borne epoxy latex resin flooring coating, the paint for railway,locomotive, bridge, and container, water borne epoxy anti-corrosion coat, domestic outfit paint and metallic paint


Storage conditions:this product should be stored sealed in a cool ventilation place with six months of quality guarantee period. The expired products can be continued to use if they are detected qualified.



The combination of WL-213 and curing agent WL-140

Film thickness: 50-60um at 80℃ for 30 mins, salt fog resistance: over 800 hours

Coating film Test


Primer Test Result

Item Test Result Test Method
Physical and Chemical Properties Original paint Uniform liquid Visual check
Paint film color Light grey Visual check
Hiding power, g/m2 80 GB/T 1720-1979
Original paint viscosity (T-4 cup at 25o) S 132s GB/T 1723-1993
Fineness, micron ≤30 GB/T1724-1979
Non-volatile matters, % 52 GB/T1725-2007
Surface drying time, min at 23℃ 20 GB 1728-1979
Hard drying time, h at 25℃ 5 GB 1728-1979
Baking time, min at 65℃ 30 GB/T1728-1979
Pot life, h at 25℃ 3 HG/T3668-2000-5.9
Mechanical Properties



H GB/T 6739-2006
Flexibility, mm 1 GB/T 1731-1993
Impact resistance, KgNaN/50cm pass GB/T 1732-1993


(20 times,320# sand paper

grindable GB/T1770-2008


(Cross-cut tape test)

1 GB/T9286-1998


(circle-cut tape test)

1 GB/ 1720-1979
Matching Compatibility with other coating Good
Corrosion resistance Water resistance at 23℃ 240 h , no bubbling, peeling off and rusting GB/T 1733-1993

Alkaline resistance

(at 25℃, 0.1N NaOH)

48 h GB/T9274-1998

Acid resistance

(at 25℃, 0.1N


48 h, no bubbling GB/T9274-1998

Oil resistance

(at 25℃,10# Transformer oil)

48 h, no change HGT/ 9274-1998
Temperature alternating resistance (at -40℃ +60℃)
Salt fog resistance (480h) Bubbling at cross, not bigger than 2 mm at a single side GB 1771-2007