| Place of Origin: | china |
|---|---|
| Brand Name: | WeiLi Resin® |
| Certification: | IOS9001 |
| Model Number: | SE3611 |
| Minimum Order Quantity: | 5000KG |
| Price: | Negotiable |
| Packaging Details: | 200kg/drum |
| Delivery Time: | 14 work days |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 500t/month |
| Appearance: | Clear, Light Yellow | Fe-Co Color: | ≤2 |
|---|---|---|---|
| Viscosity Pa.s/25℃: | 12-25 | Non-volatile %: | 60±2 |
| Acid Value MgKOH/g: | 7-12 | Solvent: | S-150#/NBA |
| Highlight: | flexible acrylic resin,liquid acrylic resin,High Fullness Thermosetting Acrylic Resin |
||
Solvent based thermosetting acrylic resin after reaction with methyl etherified amino( or partial etherified amino), the film formed after baking, has the features of high fullness, high gloss, excellent boiling resistance, good screen printing adaptability, etc, this resin can be formulated to coating or ink, it is used in metal(especially stainless steel) glass and other surface to make hardware coating, coil coating, glass ink, automotive coating, has strong decorative, alcohol and boiling water resistance.
Special recommendation: used in coating materials that require resistance to boiling.
1. Features
High gloss, high fullness, printing adaptability, screen print adaptability, good adhesion to hardware and glass, water resistance
2. Applications
Glass paint, glass ink, tin printing ink, hardware ink, hardware baking paint
3. Properties
| Component | Appearance |
Fe-Co Color |
Viscosity Pa.s/25℃ |
Non-volatile % |
Acid value mgKOH/g |
Solvent |
| Acrylic copolymer | Clear, light yellow | ≤2 | 12-25 | 60±2 | 7-12 | S-150#/NBA |
4. Compatibility and solubility
| XYL | + | BCS | + |
| Trimethylbenzene | + | CAC | + |
| BAC | + | IBA | + |
| CYC | + | NBA | + |
Remark:+ show soluble in/compatible in
5. Reference formula
| White colored top coat | Diluent | ||
| SE3611 | 40.0 | XYL | 50 |
| HE582-3 | 18.0 | Trimethylbenzene | 10 |
| BBG306 | 0.2 | BAC | 10 |
| BBG052 | 0.1 | CAC | 15 |
| Titanium dioxide | 22 | IBA | 15 |
| XYL/IBA | 18.7 | ||
| BBG110 | 1.0 | ||
6. Process conditions
▲ Baking condition: (1) 150℃ x 30min
▲ Substrate: Sand plate tin
7. Test technical index
| Test Item | Test Method | Reference Standard | Test Standard |
Test Result (reference value) |
| Hardness | Pencil scratch | GB/T6739-96 | ≥2H | 2H |
| Gloss | 60degree | GB/T9754-88 | ≥85 | 95 |
| Adhesion | The case method | GB/T9286-98 | 100% | 100% |
| Alcohol resistance | Wiping method | ------- | 200 times not grinning(500g) | 320 times(20μm) |
| Impact | Impact method | GB/T1732-93 | ≥30kg.cm | 45cm(20μm) |
| Flexibility | Bending method | GB/T1732-93 | ≥2mm | 1mm |
| Water boiling resistance | Boiling water | ------- | No color change, not bubbling, not falling off | >180min |
| Salt fog resistance | Neutral salt fog | GB/T1771-91 | Unilateral corrosion not exceeding 3mm | 148h |
| Acid resistance | Soaking method | GB/T9274-88 | 10%H2SO4 24h not bubbling, not falling off, no color change | Qualified |
| Alkaline resistance | Soaking method | GB/T9274-88 | 5%NaOH24h not bubbling, not falling off, no color change | Qualified |
8. Safe storage and shelf life
1. Stored in cool and ventilation place, keep far away from heat and fire resources, keep the container closed.
2. From production date, shelf life is 12months.
9. Packing specifications
200kg/pail (new metal pail)
10. Safety
This product contains solvent, must do safeguard procedure, handle carefully, avoid contact with the skins and eyes, for other details, please refer to MSDS of this product.