High Fullness Solvent Based Acrylic Resin For Motorcycle Finishing Coat

Basic Information
Place of Origin: china
Brand Name: WeiLi Resin®
Certification: ISO9001
Model Number: SE6672
Minimum Order Quantity: 5000KG
Price: Negotiable
Packaging Details: 200kg/drum
Delivery Time: 14 work days
Payment Terms: L/C, T/T
Supply Ability: 500t/month
Detail Information
Appearance: Clear Fe-Co Color: <1
Viscosity Pa.s/25℃: 3-6 Non-volatile %: 65±2
Acid Value MgKOH/g: 3-6 Hydroxyl Value: 100
Highlight:

clear acrylic resin

,

eco friendly resin

,

High Fullness Solvent Based Acrylic Resin


Product Description

Hydroxyl Acrylic Resin SE6672

SE6672 is recommended for varnishes and clearcoats, topcoats for steel and plastics, and high gloss one-coat metallic finishes for car refinishes and industrial applications.it exhibits good exterior durability, good build and gloss, high end hardness and good adhesion results on metallic base coats.

 

1. Features

High gloss, high fullness, excellent levelling property, fast drying, high hardness, excellent chemical resistance

 

2. Applications

PU finishing varnish, car, motorcycle finishing varnish

 

3. Properties

Component Appearance

Fe-Co

Color

Viscosity

Pa.s/25℃

Non-volatile

%

Acid value

mgKOH/g

Solvent Hydroxyl value
Acrylic copolymer Clear <1 3-6 65±2 3-6

XYL/TOL/BAC

100

 

4. Compatibility and solubility

XYL + BCS +
Trimethylbenzene + CAC +
BAC + CYC +

Remark:+ show soluble in/compatible in

 

5. Reference formula

Two component (gloss black paint Diluent
(A component))
SE6672 65 XYL 40
Carbon black powder 3 TOL 5
BYK-306 0.2 BAC 25
EFKA2018 0.1 CAC 15
EFKA4010 3 PMA 15
10%sn 0.2    
BAC/XYL 29.7    
(B component) Bayer N3390      

A component: B component: diluent=100: 14: 80~100

 

6. Process conditions

▲ Baking condition: (1) 65℃ x 60min, place 24hours for test

(2) Air drying

▲ Substrate: Sand plate tin

 

7. Test technical index

Test Item Test Method Reference Standard Test Standard

Test Result

(reference value)

Surface drying Blow cotton ball method ------ Not stick cotton ball 30min(26μm)
Hard drying Finger pressing method ------ No finger print 24h(26μm)
8h hardness Pencil scratch GB/T6739-96 ----- <HB
24h hardness Pencil scratch GB/T6739-96 ----- H
Gloss 60 degree GB/T9754-88 ≥90 98
Hardness Pencil scratch GB/T6739-96 ≥2H 2H
Impact Impact method GB/T1732-93 ≥30kg.cm 50cm(26μm)
Flexibility Bending method GB/T1731-93 ≤2mm 1mm
Adhesion The case method GB/T9286-98 100% 100%
Fullness Visual method ----- Excellent fullness, good brightness Excellent
Levelling property Visual method ----- Flat and smooth, no shrinkage cavity Qualified
Ageing resistance QUV machine -----

600h non discolouring, not

falling off, gloss loss rate≤1%

Qualified
Acid resistance Soaking method GB/T9274-88

 

10%H2SO472h

not bubbling, not falling off, not discoloring

 

 

Qualified
Alkaline resistance Soaking method GB/T9274-88

 

5%NaOH48h

not bubbling, not falling off, not discoloring

 

Qualified

 

8. Safe storage and shelf life

1. Stored in cool and ventilation place, keep far away from heat and fire resources, keep the container closed.

2. From production date, shelf life is 12months.

 

9. Packing specifications

200kg/pail (new metal pail)

 

10. Safety

This product contains solvent, must do safeguard procedure, handle carefully, avoid contact with the skins and eyes, for other details, please refer to MSDS of this product.

 

 