Water-Based Acrylic Emulsion with Superior Adhesion and Salt Fog Resistance for Metal Substrates

Name: Water-Based Acrylic Emulsion with Superior Adhesion and Salt Fog Resistance for Metal Substrates
Brand: Xiamen WangQin Chemical Technology Co., Ltd.
SKU: WL-A1000
Price: Negotiable USD
Availability: InStock

Brand Name:	WeiLi Resin®
Model Number:	WL-A1000
MOQ:	1ton
Price:	Negotiation
Payment Terms:	T/T
Supply Ability:	15t/month

Detail Information

Product Description

Detail Information

Place of Origin:

China

Certification:

ISO9001

Appearance:

Milky White Liquid

Non-volatile Content:

47 ± 1%

Viscosity:

50~500mPa·S

PH:

7.0-9.0

Minimum Film-Forming Temperature (MFFT):

40℃

Packaging Details:

120 Kg/barrel

Highlight:

water-based acrylic emulsion metal

acrylic emulsion salt fog resistance

water-based industrial coating resin

Product Description

Product Overview

WL-A1000 is an aqueous emulsion prepared by copolymerization of acrylate monomers. It offers excellent adhesion and superior resistance to water and salt spray, making it widely suitable for use in primers and topcoats across a variety of metal substrates.

Physical Properties

Property	Units	Value
Appearance	—	Milky white liquid
Non-volatile content	%	47 ± 1
Viscosity	mPa·s	50–500
pH	—	7.0–9.0
Minimum Film-Forming Temperature (MFFT)	°C	40

Key Performance Benefits

Exceptional adhesion to metal substrates
Excellent water resistance
Superior salt spray resistance

Reference Salt Spray Formulations

Table 1: Heavy Metal-Containing Formulation

No.	Name	Content	Additive Brand
1	Deionized Water	15.0	—
2	BYK-190	1.0	Dispersant / BYK
3	DMEA	0.1	pH Regulator
4	AD01	0.1	Defoamer / Evonik
5	Carbon Black M100	2.0	Carbon Black / Mitsubishi
6	Barium Sulfate	19.0	Extender Pigment
7	Strontium Chromate	1.0	Anti-corrosive Pigment
8	GEL-0434	0.2	Thickener
Grind to a fineness of ≤30 microns
9	WL-A1000	50	Anti-corrosive Emulsion
10	DH-12	2.5	Coalescent
11	ZS-83	0.1	Thickener
12	TWIN4100	0.2	Substrate Wetting Agent
13	FLASH-X 150	0.5	Flash Rust Inhibitor / HALOX
14	Deionized Water	8.3	—
Total		100.00

Table 2: Heavy Metal-Free Formulation

No.	Name	Content	Additive Brand
1	Deionized Water	8.4	—
2	BYK-190	1.5	Dispersant / BYK
3	DF110D	1.1	Defoamer / Evonik
4	S-706	20.0	Titanium Dioxide
5	Nubirox 106	3.5	Anti-corrosive Pigment / Nubiola
Grind to a fineness of ≤20 microns
6	WL-A1000	55.0	Anti-corrosive Emulsion
7	DMEA	0.5	pH Regulator
8	TEXANOL	3.0	Coalescing Agent / Eastman
9	Coa 2025	0.2	Thickener
10	Coa ZS83	0.1	Thickener
11	FLASH X 150	0.5	Flash Rust Inhibitor / HALOX
12	TEGO-270	0.2	Substrate Wetting Agent / TEGO
13	TEGO-496	0.2	Leveling Agent / TEGO
14	Deionized Water	5.8	—
Total		100.00

Tags:

Water Based Acrylic Resin

Solid Acrylic Resin

Water Based Polyester Resin

Polyethylene Wax Emulsion

Water Based Alkyd Resin

Solvent Based Acrylic Resin

Water Based Epoxy Resin

Mirror Effect Ink

Epoxy Curing Agent

Water Based Hydroxyl Acrylic Resin

Water Based Peelable Resin

High Hardness Floor Coatings

Resins For Wood Coatings

Water Based Industrial Coating Resins

Water Based Acrylic Resin

Solid Acrylic Resin

Water Based Polyester Resin

Polyethylene Wax Emulsion

Water Based Alkyd Resin

Solvent Based Acrylic Resin

Water Based Epoxy Resin

Mirror Effect Ink

Epoxy Curing Agent

Water Based Hydroxyl Acrylic Resin

Water Based Peelable Resin

High Hardness Floor Coatings

Resins For Wood Coatings

Water Based Industrial Coating Resins

products details

Water-Based Acrylic Emulsion with Superior Adhesion and Salt Fog Resistance for Metal Substrates

Water-Based Acrylic Emulsion with Superior Adhesion and Salt Fog Resistance for Metal Substrates

water-based acrylic emulsion metal