Water Based Varnish Styrene Acrylic Emulsion For PE Double Coated Paper

Basic Information
Place of Origin: China
Brand Name: WeiLi Resin®
Certification: ISO9001
Model Number: WQ-2090
Minimum Order Quantity: 5000KG
Price: Negotiable
Packaging Details: 200kg/drum
Delivery Time: 14 work days
Payment Terms: T/T, L/C
Supply Ability: 500t/month
Detail Information
Solid Content: 45±1% Appearance: Semi Translucent Emulsion
Tg: +110℃ PH: 8.0-9.0 At 25℃
Viscosity(mPa.s): 1000-2000 Acid Value: 65
MFFT: >90℃
High Light:

Varnish Styrene Acrylic Emulsion

,

PE Paper Acrylic Emulsion

,

Double Coated Paper Acrylic Emulsion


Product Description

Styrene Acrylic Emulsion For Water Based Varnish For PE Double Coated Paper

 

WQ-2090 Water Based Acrylic Emulsion

 

Introduction

WQ-2090 is a hard non-film-forming styrene-acrylic copolymer emulsion specially formulated for water-based overcoat varnishes and printing inks. The varnish formulated with this product has fast drying speed and high gloss, good water resistance and anti-stick back performance, and it has good compatibility with popular acrylic polymers on the market. Because this product cannot form a film alone, it must be used with a suitable film-forming aids or mixed with a film-forming acrylic emulsion with a smaller particle size, such as used with our film-forming varnish emulsion WQ-2027, WQ-2024, WQ-2018, WQ-2015, etc. Besides, in flexo and gravure inks, the product has excellent pigment wetting.

 

Physical Property:

Appearance Translucent milky emulsion
Solid content (%) 45±1
Viscosity at 25℃,cps(Brookfield, LVT No.4,60 RPM ) 1000-2000
Acid value 65
pH value 8.0-9.0
Density(g/l) 1.02-1.05
Particle size(μm) 0.20-0.30
MFFT (℃) >90
Tg(℃) +110

 

Performance

  • High gloss, when properly formulated, it can produce very high gloss and excellent clarity
  • Good wetting of pigments
  • Fast drying speed
  • Excellent water and stick resistance, retains original gloss when wet surface dries
  • Good brush and abrasion resistance
  • Low odor
  •  

Application

  • Water-based overprint varnish
  • Water-based flexo, gravure ink
  • Suitable for water-based plastic inks
  • Suitable for all types of water-based varnishes and all types of high-grade water-based inks

 

Suggested formula for water-based varnish
Water Based Varnish For PE double-coated paper (Flexography)
No. Raw Materials %  
WQ-2090 (non-film forming) 11.00  
WQ-2028 (water resistance/ improve gloss) 10.00  
Deionized water 5.00  
WQ-2015 (film-forming) 63.00  
⑤ * DOWSIL™ 51 2.00 Dow Corning
Waterproof Wax Emulsion 8.00 WQ-W40 or local supplier
Defoamer 1.00 TEGO Foamex 825
Total 100.00  
Remark:
1. The process of adding raw materials: ① + ② + ③, first add these three raw materials while stirring , + ④ + ⑤ , finally add wax emulsion and defoamer while stirring + ⑥ + ⑦
Stirring time: about 30 minutes, 300 rpm/min.
2. *: DOWSIL™ 51 needed to be diluted with Ethanol =1:1
3. 4# cup: 25 ± 5s
PH value: 8.30 ± 0.5
4. Final inks: varnish 50%+pigment paste 50% =100 (Ajusting it accoring to needs)

Test Standards for inks:
① Ice resistance: Ice is placed for 10 minutes and wipe 15 times without decoloring as qualified.
② N-hexane resistance: 15 minutes of immersion without decoloring is qualified.
③ 4% Acetic acid resistance: Rub 15 times without decoloring as qualified.
④ Saliva resistance: Rub 15 times without decoloring as qualified.
⑤ Sauce resistance : Rub15 times without decoloring is qualified.
⑥ Edible oil resistance: Rub15 times without decoloring is qualified.

Storage

Store in a closed container and avoid freezing and high temperature. Suggested normal storage temperature is 10 to 35℃.

 

Packing

200KG/Drum.

 

Special Tips

This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.

 

 

 