Self Crosslinking Styrene Acrylic Copolymer For Water Based Gravure Ink Varnish

Basic Information
Place of Origin: China
Brand Name: WeiLi Resin®
Certification: ISO9001
Model Number: WQ-2217
Minimum Order Quantity: 5000KG
Price: Negotiable
Packaging Details: 200kg/drum
Delivery Time: 14 work days
Payment Terms: L/C, T/T
Supply Ability: 500t/month
Detail Information
Appearance: Translucent Milky White Solid Content: 45±1%
Tg (℃): 0 Viscosity: 200-1000 MPa.s
PH (25℃): 8.5 MFFT(℃): >0
High Light:

Self Crosslinking Styrene Acrylic Copolymer

,

Gravure Ink Styrene Acrylic Copolymer

,

Gravure Ink Varnish Acrylic Copolymer


Product Description

WQ-2217 Water Based Acrylic Emulsion

 

Self-Crosslinking Styrene-Acrylic Copolymer For Water Based Gravure Ink Varnish For Pvc Film Wallpaper

Introduction

It is a room temperature self-crosslinking film-forming styrene-acrylic copolymer emulsion synthesized by a new generation of polymer polymerization process. It is specially designed for water-based gravure printing inks. It has good compatibility with the popular acrylic polymers on the market. In addition, in gravure inks, it has good pigment wetting ability.

 

Physical Property:

Apperance Translucent liquid
Solid content % 45±1
Viscosity at 25℃,cps(Brookfield, LVT No.4,60 RPM ) 200-1000
Ph Value 8.0-9.0
Density (g/l) 1.02-1.05
Particle size(μm) 0.20-0.30
Glass field temperature,TG(℃) 0

 

Features

  • Excellent film formation and long-lasting adhesion
  • Excellent transparency, this product can produce a high-gloss transparent film on the surface of the substrate
  • Good compatibility with popular water-based resins on the market
  • Low odor, low VOC
  • Unlimited amount of ethanol can be added
  • Water resistance is particularly good

 

Application

  • It is applied on various substrates like PE, LDPE, HDPE, BOPP, PET film;.
  • Suitable for all kinds of high-grade water-based inks, gravure printing
  • Water-based gravure ink
  • Water-based plastic ink

 

 

Water Based Varnish For PVC & Film & Wallpaper (Gravure)
  No. Raw Materials %  
  WQ-2217 (film-forming) 50.00  
  WQ-2021 (acrylic resin solution) 10.70  
  WQ-290 (non-film forming) 13.00  
  DOWSIL™ 51 : Ethanol (1:1) * 1.00 Dow Corning
  Wax emulsion 4.00  
  Defoamer 0.30  
  Ethanol 21.00  
  Total 100.00  
  Technological process:
1. ①+②+③+④+ ⑤+⑥, add the above materials and stir at the same time, at a constant speed, finally add ⑦, stirring time: about 30 minutes/300 rpm.
2. *: DOW CORNING DOWSIL™ 51 Additive diluted with Ethanol =1:1
3. 4#cup: 11 seconds ± 2
PH value: 8.30 ± 0.5
3. Special notes: Please do not directly add ethanol. When the mixer is stirring at a slow speed, slowly add ethanol, the effect is better (Because directly adding ethanol will cause demulsification and slag).
4. Final inks: - (Ajusting it accoring to needs)
varnish 75%+pigment paste 25% =100
Note: The pigment paste is mixed slowly and finially, the effect is the most friendly.

 

 

Storage Condition

The product should be stored in an airtight container to avoid freezing and high temperature. Recommended normal storage temperature is 10-35°

 

Special Tips

This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.

 

 

 

Contact Details
WQ Chemical

Phone Number : +8613906014499

WhatsApp : +8619906019236