Non Film Forming Styrene Acrylic Polymer Emulsion For PE Plastic Printing Inks

Name: Non Film Forming Styrene Acrylic Polymer Emulsion For PE Plastic Printing Inks
Brand: Xiamen WangQin Chemical Technology Co., Ltd.
SKU: WQ-2011
Availability: InStock

Brand Name:	WeiLi Resin®
Model Number:	WQ-2011
MOQ:	5000KG
Price:	Negotiable
Payment Terms:	L/C, T/T
Supply Ability:	500t/month

Detail Information

Product Description

Detail Information

Place of Origin:

China

Certification:

ISO9001

Appearance:

Opaque Emulsion

Solid Content (%):

47±1

Viscosity:

800-1500 MPa*s

Acid Value:

PH:

8.0-9.0, 25℃

Tg:

98℃

Alternative:

Joncryl 89

Packaging Details:

200kg/drum

Highlight:

Styrene Acrylic Polymer Emulsion

Non Film Forming Acrylic Resin

Inks Styrene Acrylic Polymer Emulsion

Product Description

Chinese Non Film Forming Styrene Acrylic Polymer Emulsion For PE Plastic Printing Inks

Introduction
WQ-2011 non-film forming, hard styrene and acrylic copolymer emulsion, which is specifically formulated for water based overprint varnishes and printing inks.

WQ-2011 and Joncryl 89 has similar performance and physical properties. WQ-2011 acrylic polymer has high gloss and clarity, non-blocking and fast drying properties for OPV and printing inks. The varnish formulated with WQ-2011 has fast drying, excellent re-solubility and high gloss, excellent water resistance and anti-sticking properties. Also it has good pigment wetting in flexography and gravure inks.

Physical Property:

Appearance opaque emulsion
Non-volatile %: 47
pH 8.0-9.0
Viscosity cps :800-1500
Acid number (NV) 51
Density g/cm³ :1.05
MFFT °C :> 90
Tg °C :98
Freeze-thaw stable :Yes

Performance:

High gloss, fast drying, suitable for ink and varnish
High clarity
Good resisitance to heat and abrasion
Good anti-sticking (non-blocking)
Excellent re-solubility

Reference Formulation Water Based Varnish For Plastic Substrate (Flexography)

No.	Raw Materials	%
①	WQ-2015 (film-forming)	70.00
②	WQ-2011 (non-film forming)	19.00
③	WQ-2028 (improving gloss)	5.50
④	Wax emulsion	4.00
⑤	DOWSIL™ 51 : Ethanol (1:1) *	1.00	Dow Corning
⑥	Defoamer	0.50	TEGO Foamex 825
Total		100.00
Remark: 1. ①＋②＋③+④+⑤＋⑥ Add the above materials and stir at the same time, at a constant speed, stirring time: about 30 minutes/300 rpm. 2. *: DOWSIL™ 51 Additive diluted with Ethanol =1:1 3. 4# cup: 25 seconds ± 2 PH value: 8.20 ± 0.5% 4. Final inks: varnish 70%+pigment paste 30% =100 (Ajusting it accoring to needs)

Application

Flexo and gravure printing inks
Overprint varnish

Packing

IBC
200KG/Drum.

Tags:

Water Based Acrylic Resin

Solid Acrylic Resin

Water Based Polyester Resin

Polyethylene Wax Emulsion

Water Based Alkyd Resin

Solvent Based Acrylic Resin

Water Based Epoxy Resin

Mirror Effect Ink

Epoxy Curing Agent

Water Based Hydroxyl Acrylic Resin

Water Based Peelable Resin

High Hardness Floor Coatings

Resins For Wood Coatings

Water Based Industrial Coating Resins

Water Based Acrylic Resin

Solid Acrylic Resin

Water Based Polyester Resin

Polyethylene Wax Emulsion

Water Based Alkyd Resin

Solvent Based Acrylic Resin

Water Based Epoxy Resin

Mirror Effect Ink

Epoxy Curing Agent

Water Based Hydroxyl Acrylic Resin

Water Based Peelable Resin

High Hardness Floor Coatings

Resins For Wood Coatings

Water Based Industrial Coating Resins

products details

Non Film Forming Styrene Acrylic Polymer Emulsion For PE Plastic Printing Inks

Non Film Forming Styrene Acrylic Polymer Emulsion For PE Plastic Printing Inks

Styrene Acrylic Polymer Emulsion

Non Film Forming Acrylic Resin

Inks Styrene Acrylic Polymer Emulsion