Type Of Polymer: | Waterborne Epoxy Modified Acrylic Dispersion | Non-volatile(%): | 32±2 |
---|---|---|---|
Viscosity( 25℃, Mpa*s): | ≤2000 | PH: | 8.0-10.0 |
Neutral.agent: | DMEA | OH Value On Solids (mgKOH/g): | ---- |
Highlight: | modified epoxy resin,epoxy emulsion,Water Soluble Epoxy Modified Acrylic Resin |
Waterborne Epoxy Modified Acrylic Resinwl-132 is widely used in industrial and metal coatings due to its quick drying, low odor and environmental protection. Using anti-rust and anti-corrosion paint produced by WL-132, it not only has good performance, but also has short working period, can realize double guarantee of quality and efficiency.
WL-132 is stable to high shear speed and can be directly used for pigment paste grinding.
It is recommended for metal protection projects which require short and fast construction period.
1, Product Composition:
Waterborne Epoxy Modified Acrylic Resin, Cosolvent
2, Typical Data:
Type of polymer | Waterborne epoxy modified acrylic dispersion |
Non-volatile(%) | 32±2 |
Viscosity( 25℃, mpa*s) | ≤2000 |
PH | 8.0-10.0 |
Neutral.agent | DMEA |
OH value on solids (mgKOH/g) | ---- |
Air dry | Applicable (Oxidation Cross-linking) |
Cross-Linking with amino resin | Inapplicable |
Grinding | Applicable |
Drying speed | better |
Corrosion resistance | better |
weatherability | better |
3, Product Properties:
High temperature baking coatings with amino-resin, fast baking speed
Good storage stability.
4, Instructions:
WL-132 can be diluted with water after neutralization by N,N-dimethyl ethanolamine. It has to combine waterborne amino resin to make bakingcoating. The suggested amount is about 20-40% of WL-132 by weight. The neutralizing agent s generally N,N-dimethyl ethanolamine andadded about 7% ofWL-132. In order to have better adhesion in glass, you must add the silane coupling agent before using. The bakingtemperature is suggested 150-180℃ and the baking time is 20-30min. Viscosity of the dispersion will increase as the pH value increases.
5, Storage:
It is suggested that the product should be stored in a cool and dry place. The quality guarantee period is 6 months, and the expired products canstill be used after passing the inspections.
6, Applications:
Waterborne baking coatings for glass.
7, Note:
the specification is a general introduction to the products of our company. It will be adjusted with the product improvement. Please contact with thecompany to obtain the latest product description.