Water Based Hydroxyfunctional Polyacrylic Resin with 3.9% Hydroxyl Value Excellent Water Resistance 15 Days and 50/50 cm kg Impact Resistance

Brand Name:	WeiLi
Model Number:	WL-AD3940
MOQ:	5000KGS
Price:	Negotiable
Payment Terms:	T/T
Supply Ability:	500TONS

Detail Information

Product Description

Detail Information

Place of Origin:

China

Certification:

ISO9001

Hydroxyl Value(%):

3.9

Advantage:

Suitable For High Temperature And Low Humidity Environment

Feature:

Could Be Used With Solvent/water Based Curing Agent

Performance:

Excellent Water Resistance（15days）

Impact (front/back Cm Kg):

50/50

Packaging Details:

plastic drum

Highlight:

Water Based Hydroxyfunctional Resin

Component construction Hydroxyfunctional Resin

Water Based Hydroxyfunctional Polyacrylic Resin

Product Description

Water Based Hydroxyfunctional Polyacrylic Resin For Large Component Construction

Product Introduction

This water-based hydroxylated acrylic dispersion is designed for use with solvent-based or water-based isocyanate curing agents to create high-performance two-component polyurethane coatings. It is specifically formulated for topcoats on various metal substrates.

With a hydroxyl content of WEI 3.9%, this resin is particularly suitable for construction environments with high temperature and low humidity conditions. It offers excellent cost-effectiveness when paired with an oily curing agent.

Key Features

Excellent compatibility with solvent-based isocyanate curing agents
Superior water resistance properties
Extended application period

Physical Properties

Property	Value	Detection Method
Appearance	Milky white liquid	Visual
Non-volatile matter (%)	44±2	GB/T 1725-2007
Viscosity (mPa*S)	200-3000	GB/T 21059-2007
PH	7.5~8.5	GB/T 9724-2007
Hydroxyl value (%)	3.9	Based on solids

Note: Product viscosity is affected by pH value - as pH increases, viscosity and thixotropy will increase.

Paint Film Properties (with solvent curing agents)

Property	Value (WL-AD3940/TPA100 Diluted by BGA)
25°C/35% outdoor drying time	60min
14.5°C/60% outdoor drying time	120min
Water resistance at room temperature	15 days
Pencil hardness (baking)	H
Bending resistance (mm)	<1
Impact (front/back cm kg)	50/50
Effective opening period at 35°C	4h

Special Note: This material is developed according to our existing technology and experience. While we provide sincere technical advice, we cannot guarantee its performance in all samples and formulations. All data provided is for reference only.

Tags:

Water Based Acrylic Resin

Solid Acrylic Resin

Water Based Polyester Resin

Polyethylene Wax Emulsion

Water Based Alkyd Resin

Solvent Based Acrylic Resin

Water Based Epoxy Resin

Mirror Effect Ink

Epoxy Curing Agent

Water Based Hydroxyl Acrylic Resin

Water Based Peelable Resin

High Hardness Floor Coatings

Resins For Wood Coatings

Water Based Industrial Coating Resins

Water Based Acrylic Resin

Solid Acrylic Resin

Water Based Polyester Resin

Polyethylene Wax Emulsion

Water Based Alkyd Resin

Solvent Based Acrylic Resin

Water Based Epoxy Resin

Mirror Effect Ink

Epoxy Curing Agent

Water Based Hydroxyl Acrylic Resin

Water Based Peelable Resin

High Hardness Floor Coatings

Resins For Wood Coatings

Water Based Industrial Coating Resins

products details

Water Based Hydroxyfunctional Polyacrylic Resin with 3.9% Hydroxyl Value Excellent Water Resistance 15 Days and 50/50 cm kg Impact Resistance

Water Based Hydroxyfunctional Polyacrylic Resin with 3.9% Hydroxyl Value Excellent Water Resistance 15 Days and 50/50 cm kg Impact Resistance

Water Based Hydroxyfunctional Resin

Component construction Hydroxyfunctional Resin

Water Based Hydroxyfunctional Polyacrylic Resin