Low VOC Waterborne Hydroxyl Acrylic Resin with 72±2 Non-volatile and 137 mgKOH/g OH Value for Topcoating

Name: Low VOC Waterborne Hydroxyl Acrylic Resin with 72±2 Non-volatile and 137 mgKOH/g OH Value for Topcoating
Brand: Xiamen WangQin Chemical Technology Co., Ltd.
SKU: WL-158
Availability: InStock

Brand Name:	WeiLi Resin®
Model Number:	WL-158
MOQ:	5000KG
Price:	Negotiable
Payment Terms:	L/C,T/T
Supply Ability:	500t/month

Detail Information

Product Description

Detail Information

Place of Origin:

china

Certification:

ISO9001

Type Of Polymer:

Waterborne Hydroxyl Acrylic Dispersion

Non-volatile(%):

72±2

Viscosity( 25℃, Mpa*s):

50-280

Neutral.agent:

DMEA

OH Value On Solids (mgKOH/g):

137

Quality Guarantee Period:

6 Months

Packaging Details:

200kg/drum

Highlight:

two part acrylic resin

acrylic resins for coatings

Waterborne Hydroxyl Acrylic Resin

Product Description

Low VOC Waterborne Hydroxyl Acrylic Resin Silicone Modified Acrylic Resin For Topcoating

Waterborne silicone modified hydroxyl acrylic dispersion WL-158

Low-VOC waterborne polyurethane paints formulated with this resin match or exceed the performance of solventborne polyurethane paints for metal applications. These two-component waterborne polyurethanes combine a waterborne polyacrylate with a water-dispersible polyisocyanate, delivering superior hardness, impact resistance, solvent resistance, and accelerated weathering performance comparable to standard solventborne polyurethane coatings.

Product Composition

Waterborne hydroxyl Acrylic resin, Cosolvent, without Neutralizing Agent, Water.

Typical Data

Type of polymer	Waterborne hydroxyl acrylic dispersion
Non-volatile(%)	72±2
Viscosity(25℃, mpa*s)	50-280
PH
Neutral.agent	DMEA
OH value on solids (mgKOH/g)	137
Air dry	Applicable(for 2K PU)
Cross-Linking with amino resin	Applicable, can be with solvent curing agent
Grinding	Applicable
Particle charge	Anionic
Drying speed	very good
Tolerance	very good

Product Properties

Self emulsifying process, emulsifier free
Excellent shear stability, can be grinded with dispersions directly
Good gloss, high film thickness without blister
Excellent weather resistance, water resistance and aging resistance

Instructions

WL-158 can be diluted with deionized water to construction viscosity. The resin helps wet pigments, though wetting agents may reduce PH value. The coating system's PH can be adjusted using N,N-dimthylethanolamine, with viscosity increasing as PH rises.

When mixed with poly aliphatic isocyanate curing agent (e.g., BAYHYDUR 304 at NCO/OH=1.4/1.0), WL-158 produces high-gloss top coatings that dry quickly at room temperature or force-dry at 80°C (activation period ~3 hours).

Construction equipment can be cleaned with water, alkaline detergent, or water-soluble solvent.

Storage

Store in a cool, dry, weak alkaline environment. Quality guarantee period is 6 months, though expired products may still be used after passing inspections.

Applications

2KPU self-drying top coatings and amino-baking top coatings.

Note

Specifications represent general product information and may change with product improvements. Contact us for the latest product description.

Tags:

Water Based Acrylic Resin

Solid Acrylic Resin

Water Based Polyester Resin

Polyethylene Wax Emulsion

Water Based Alkyd Resin

Solvent Based Acrylic Resin

Water Based Epoxy Resin

Mirror Effect Ink

Epoxy Curing Agent

Water Based Hydroxyl Acrylic Resin

Water Based Peelable Resin

High Hardness Floor Coatings

Resins For Wood Coatings

Water Based Industrial Coating Resins

Water Based Acrylic Resin

Solid Acrylic Resin

Water Based Polyester Resin

Polyethylene Wax Emulsion

Water Based Alkyd Resin

Solvent Based Acrylic Resin

Water Based Epoxy Resin

Mirror Effect Ink

Epoxy Curing Agent

Water Based Hydroxyl Acrylic Resin

Water Based Peelable Resin

High Hardness Floor Coatings

Resins For Wood Coatings

Water Based Industrial Coating Resins

products details

Low VOC Waterborne Hydroxyl Acrylic Resin with 72±2 Non-volatile and 137 mgKOH/g OH Value for Topcoating

Low VOC Waterborne Hydroxyl Acrylic Resin with 72±2 Non-volatile and 137 mgKOH/g OH Value for Topcoating

two part acrylic resin

acrylic resins for coatings

Waterborne Hydroxyl Acrylic Resin