|Emulsion Composition:||Water Based Alkyd Resin, Cosolvent,neutralizer, Water||Apprearance:||White To Light Brown Emulsion|
|Non-Volatile Matters (GB/T 1725:||42±2%||Viscosity(mPa.s):||<2000 MPa.s（Rotary Viscometer）|
|Neutral Agent:||DMEA||Dry:||Self Drying|
Waterborne Alkyed Resin,
Water based Alkyed Resin,
Modified Alkyd Resin
WL-0310B-11 Waterborne Alkyed Resin
WL-0310B-11 waterborne acrylic modified alkyd dispersions have excellent brush, roller and spray application performance. Due to the leveling properties of alkyd resins and adhesion to various substrates, it is easy to obtain high gloss. Through oxidative cross-linking (depending on humidity and temperature), excellent chemical resistance, hardness development and water resistance can be formed in a short time. It is an environmentally friendly product with low resin VOC. It can be made primer and paint for metal surface, such as oxidized Iron Red Paint.
|<2000 mPa.s(Rotary viscometer)||42.0 ± 2% (120℃/30min)||white to light brown liquid|
WL-0310B-11s can be used to replace solvent-based alkyd resins. On the one hand, it can be used for self-drying products, such as the development of anti-corrosion and anti-rust primers, water-based mixed paints, and it can also be used to produce low temperature Baking paint
Suggested storage temperature is 0-40℃. Best be used within half of a year after it is produced. It can be used if the product conform to the standard after half of a year .
This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.