Component: | Acrylic Copolymer | Appearance: | Light Yellow Transparent Viscous Liquid |
---|---|---|---|
Non-volatile %: | 65±2 | Acid Value MgKOH/g: | ≤60 |
Solvent: | ETB, BCS | Viscosity (Cps/ 25℃): | ≤3000-6000 |
Color: | ≤4# | PH: | 7.0-7.5 |
High Light: | Acetone Resistance Acrylic Copolymer,Butanone Resistance Acrylic Copolymer,Hardware Baking Paints Acrylic Copolymer |
WQ-99 Water Based Acrylic Resin For Baking paint
WQ-99 acrylic resin for baking apint has high gloss, high fullness, high hardness(3H), excellent solvent resistance, good butanone resistance, acetone resistance, good grease resistance, can pass 0 T-bend, high pigment-to-base ratio, oleophobic and hydrophobic. WQ-99 aclic resin can be used as anti-graffiti paint and water-based hardware paints with high performance requirements, electric vehicle baking paints, aluminum alloy baking paints, copper door baking paints.
Physical Property
Component | Appearance |
Fe-Co Color |
Viscosity Pa.s/25℃ |
Non-volatile % |
Acid value mgKOH/g |
PH (After alkali neutralization) | Solvent |
Acrylic copolymer | Light yellow transparent viscous liquid | ≤4# | ≤3000-6000 | 65±2 | ≤60 | 7.0-7.5 | ETB, BCS |
Solubility
Good solubility in N-butanol, ethylene glycol monobutyl ether, propylene glycol ethyl ether and other solvents. When using, please test the stability of the resin in the solvent and the effect of the solvent on the paint film.
Reference formula
White colored top coat | |
Raw material | Added Amount(%) |
WQ-99 | 40.0 |
Cytec 325 (Amino Resin) | 5.6 |
Leveling agent | 0.22 |
solvent | the amount of solvent should be added according to the viscosity of screen printing |
Process conditions
Test technical index
Test Item |
Test Method |
Reference Standard |
Test Standard |
Test Result (reference value) |
Hardness | Pencil scratch | GB/T6739-96 | ≥3H | 4H |
Gloss | 60degree | GB/T9754-88 | ≥85 | 85 |
Adhesion | The case method | GB/T9286-98 | 100% | 100% |
Alcohol resistance |
Wiping method |
------- |
200 times not grinning(500g) |
320 times |
Impact | Impact method | GB/T1732-93 | ≥30kg.cm |
100cm(front) 45cm(reverse side) |
Flexibility | T-Bending | ---------- | 0 grade | 0 grade |
Water boiling resistance |
Boiling water |
------- |
No color change, not bubbling, not falling off |
120min |
Butanone resistance |
soaking |
------- |
No blistering, no softening |
6h |
Packing And Safe storage