| Type Of Polymer: | Milky White Emulsion | ||
|---|---|---|---|
| High Light: | 2k Water Based Epoxy Resin,Anti Corrosion Water Based Epoxy Resin,2k Waterborne Epoxy Resin |
||
2k Water Based Epoxy Resin Fast Drying Anti Corrosion Waterborne Epoxy Resin
WL-213 Waterborne Epoxy Resin
Physical Property:
| Item | Value | Testing Method |
| Appearance | Milky white emulsion | Visual |
| Solid content | 50±2% | 30min@120℃ |
| Viscosity(mPa.s) | ≤2000 | NDJ-79 Rotational viscometer |
| PH | 7-8 | PH Meter |
| TG/℃ | 0.18-0.22 | Acetone hydrochloride method |
Performance:
| Gray paint | Surface Drying | Real Drying | Hardness | Flexibility | Adhesion | Construction Time Limit | Impact Resistance |
|
WL-213+WL-140
|
35mins | 5h | ≥H | 1grade | 0grade | ≥4h | 50cm |
◆ 80℃ X 120 minutes flash dry
◆ 14 days natural dry curing period
◆ Film thickness 50~60μm
◆ Salt spray resistance>800hrs
23-29um, baking at 80℃ for 30 minutes,
0.1mol/L NaOH aqueous solution
After 64h of alkali resistance testing :
Has spots Almost no spots
(AP resin) (WL-213/WL-140)
Thickness of film is 23-29um, back at 80℃ for 30 minutes,
0.1mol/L H2SO4 aqueous solution
Large bubbles on the board Small bubbles or no bubbles
( AP resin) (WL-213/WL-140)
3.Epoxy white paint performance comparison
| Gray paint | Surface Drying | Real Drying | Hardness | Flexibility | Adhesion | Construction Time Limit | Impact Resistance |
| Comparative resin | 37mins | 5.4h | H | 1 grade | 0 grade | 50cm | |
|
WL-213+WL-140
|
35mins | 5h | H | 1 grade | 0 grade | ≥4h | 50cm |
Thickness of film is 23-26um, back at 80℃ for 30 minutes
Failed after 30 wipes Pass after 50 wipes
(Contrast resin) (WL-213/WL-140)
The film thickness all is 23-29um, after 80℃X30 minutes
Put it into 0.1mol/L NaOH aqueous solution and soak for 64 hours
The paint surface of WL-213/WL-140 is slightly dull
The paint surface of the contrast resin has more large bubbles
After 64h of alkali resistance testing :
( AP resin) (WL-213/WL-140)
-The thickness of the film is 23-29um, after drying at 80℃ for 30 minutes
-Put into 0.1mol/L sulfuric acid aqueous solution
-After 64 hours of soaking
-The paint surface of WL-213/WL-140 is slightly dull
-The paint surface of the contrast resin has large bubbles and cracks
( contrast resin) (WL-213/WL-140)
-The film thickness is 50-60um
-Test after 7 days in a constant temperature and humidity environment
-After 64 hours of salt spray resistance test, the white paint board of the contrast resin is corroded more
( contrast resin) (WL-213/WL-140)
Special Tips
This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.